3d Printing Resin Platinum Lcd Series Solid Resin Pack
3d
£456.39
Price
£203.78
Product Description
Description
Formfutura Platinum LCD Series is a general purpose photopolymer LCD resin that is specifically developed to work with all open source LCD and DLP 3D printers in the range of 385 420nm. Our Platinum LCD resin is almost odorless and 3D prints with extremely high accuracy and a very smooth surface finish. The Platinum LCD Resin series is developed to 3D print with relatively short curing times.
Key features
- Almost no odour andnbsp; Compared to other resins on the market our Platinum LCD resin is relatively odour free!
- UV weather resistant
- Fast printing with short curing times
- High resolution 3D printing with fine detail
-
Vivid colors with an extremely high level of colorfastness
- Truly opaque and translucent colors available
- No discoloration and/or yellowing
- Excellentandnbsp;dimensional accuracy and low shrinkage
- Low water absorption
- Compatible with all open source LCD and DLP in the range of 385 420nm
The Platinum LCD Series Solid Resin Pack contains theandnbsp;Solid Blackandnbsp;Solid Whiteandnbsp;Solid Light Greyandnbsp;resins ( 500g each)
Applications
- Figurines and models
- Functional prototyping
- End use products
Resin properties (uncured liquid)
- Viscosity: 500 cps at 25anddeg;C
- Density: 1.18 g/cm2
Mechanical properties
Test method on post cured objects through 10 minutes high power mercury curing.
Properties | Typicalandnbsp; Value | Test Method |
---|---|---|
Glass transition temperature (Tg) | 51anddeg;C | ASTM D7028 |
Water absorption | 0.4% | ASTM D570 98 |
Impact strength (IZOD notched) | 18 J/m | ASTM D256A |
Tensile strength | 45 MPa | ASTM D638M |
Tensile Modulus | 1000 MPa | ASTM D638M |
Elongation at break | 8% | ASTM D638M |
Flexural Strength | 66 MPa | ASTM D790M |
Flexural Modulus | 1800 MPa | ASTM D2240 |
Shore D Hardness | 82 | ASTM D2240 |
andnbsp;Please note that the above displayed values can vary with individual machine processing post curing parts andnbsp;geometry print orientation print settings and temperature.
Preparation(s) before starting to print
- Shake the bottle for at least 2 minutes before each use.
-
After shaking the bottle leave the resin to rest for 10 minutes to let air bubbles get out of the resin
- The resin can be poured back from the vat into the bottle once your print is finished
- Always use protective measurements like safety glasses and nitrile gloves when handling resins.
General printing guidelines
Base Curing Times at 50 micron
- Translucent Black: 12sec
- Translucent Aquamarine: 10sec
- Translucent Blue: 12sec
- Translucent Red: 11sec
- Solid White: 12sec
- Solid Black: 14sec
- Solid Light Grey: 13sec
andnbsp;Post processing
-
We do advise you to post process your 3D print in order to achieve the material properties
- Rinse your 3D printed object in IPA or (Bio)Ethanol for approximately 5 minutes
-
An ultrasonic cleaner is preferred/recommended
- Make sure that IPA and/or (Bio)Ethanol rinsed objects are perfectly dry before further post curing
-
Place the rinsed parts in a well ventilated area for at least 30 minutes or use pressurized air for at least 2 minutes
- Cure your object in a high power curing chamber for approximately 20 30 minutes at 65anddeg; C
- The preferred curing wavelength is between 300 410nm
Safety